抗氯离子渗透试验装置

　　腾达试验仪器厂：

　　环氧涂层预应力钢绞线氯化物抗渗性试验装置性能特点

　　1放置115mL馏水的隔闻；

　　2一带24mm开口的两块玻璃板之间的环氧涂腰

　　3—放置175mL浓度为3mol/L的NaCl水溶液的隔间；

　　4—水平标记；

　　5-25mm的中心开口。

　　I.Performance characteristics of epoxy coating prestressed steel strａnd chloride impermeability test device

　　1 Place aside 115mL of distilled water;

　　2 an epoxy waist between two glass plates with a 24mm opening

　　3—Place a 175 mL compartment of a 3 mol/L NaCl aqueous solution;

　　4—horizontal mark;

　　5-25mm center opening.

　　试验装置：

　　两个隔间被两块玻璃板隔开，每块玻璃板的中心位置都有一个直径为24mm的开口。试样被夹在

　　两块玻璃板之间，在开口处形成一个隔膜。当两个隔间中的液体体积分别为115mL和175mL时，两

　　个隔间的液面水平线平齐。夹持隔膜的开口应浸没在溶液中。

　　A.1.2.1.2能测定氯离子浓度小于1×10-4mol/L的氯离子计。

　　A.1.2.2试样

　　试样为无金属基体的已固化的方形环氧涂层，尺寸为100mm×100mm,厚度为9.1规定的最小厚度

　　A.1.2.3步骤

　　试样放置在容器中的两块玻璃板之间，其中心位于玻璃板的开口处。在大隔间注入175mL浓度

　　为3mol/L的NaC水溶液，小隔间注入115mL蒸馏水。在23℃±2℃的温度下试验45d后，测量小

　　隔间水溶液中的氯离子浓度

　　A.1.2.4试验评定

　　小隔问水溶液中的氯离子浓度应小于1×10mol/L

　　Second,the test device

　　The two compartments are separated by two glass panels,each having a 24 mm diameter opening in the center.The sample is clamped

　　Between the two glass plates,a diaphragm is formed at the opening.When the volume of liquid in the two compartments is 115mL and 175mL,respectively,

　　The level of the liquid level in each compartment is flush.The opening holding the diaphragm should be completely submerged in the solution.

　　A.1.2.1.2 A chloride ion meter capable of measuring a chloride ion concentration of less than 1 x 10-4 mol/L.

　　A.1.2.2 sample

　　The sample is a cured metal epoxy coating with a metal-free matrix measuring 100 mm x 100 mm and a minimum thickness specified in 9.1.

　　A.1.2.3 steps

　　The sample is placed between two glass plates in the container,the center of which is located at the opening of the glass plate.Inject 175mL concentration into the large compartment

　　It was a 3 mol/L aqueous solution of NaC,ａnd 115 mL of distilled water was injected into the small compartment.Small measurement after 45 days at 23°C±2°C

　　Chloride ion concentration in aqueous solution

　　A.1.2.4 Test evaluation

　　The chloride ion concentration in the aqueous solution should be less than 1×10mol/L.

　　gbt 21073-2007环氧涂层七丝预应力钢绞线

　　Gbt 21073-2007 Epoxy coated seven-wire prestressed steel strand